老客户使用后拍图（实例一）：

修复翻新前，有一定程度的龟裂，细纹：

四周仔细贴上美纹纸，开始耐心打磨

打磨完毕后，用蒸发杯蒸上镀膜液

无需等待，蒸好两分钟即可上路

老客户使用后拍图（实例二）：

新手必读操作要点:

1、（打磨时加点水磨起来更易）打磨时先用320#砂纸用点力粗磨10分钟，把旧黄迹和龟裂痕彻底磨掉，再分别用400#、600#砂纸各磨5分钟然后用800#或1000#沙纸细磨一会，磨完后用干布把大灯上的水擦干仔细检查沙纸痕迹是否粗细统一均匀，雾化抛光前最好能用热风筒将灯面吹干加热一下效果更好，干得更快。

2、喷前要先把气管扳直,使管口向上，因为热雾气碰到冷管壁会形成水珠，管口向下水珠会滴在灯上会影响效果，雾化杯所喷到的地方若已通透晶亮即不能多次覆盖，像喷油一样讲究厚薄均匀、快慢协调。喷完后十来分钟就可以干,不粘尘,但不能刮,让它几小时后自然固化.

3、每次倒入雾化杯的雾化剂的量最好在80至100毫升之间，为防止雾化杯干烧，用完后剩下雾化剂的可用纸杯装好后再倒回玻璃瓶供下次再用。雾气喷出时间一般是加热后5到6分钟，雾气喷出时很多时候是看不到的，时间一到就可以进行雾化抛光操作，予防浪费。两个灯的雾化工作尽量控制在2到3分钟内完成，多喷要很久才能干和硬并容易出现光丝。

4、大灯的厚度一般在4到5毫米之间，龟裂层深度通常在0.1到0.4毫米左右，所以细磨多几遍也无防。

5、雾化抛光时间选择在中午前比较好,因为离晚上开大灯时有几小时的硬化时间。下午或晚上操作因离开灯时间太短,灯罩表里硬度不一,开灯受热后冷缩热胀程度也不一,效果自然欠佳

1, (polished add some water mill up more easily) when grinding with 320 # sandpaper with point force rough grinding for 10 minutes, the old yellow trace and crack completely worn, and then were 400 #, 600 # sandpaper grinding 5 minutes And then use 800 # or 1000 # sand paper fine grinding for a while, after grinding with a dry cloth to dry the water on the headlamps carefully check whether the uniformity of sandpaper traces of uniform thickness, the best can be used before the atomizer polishing lamp Drying surface heating effect is better, faster.

2, spray straight before the trachea straight, so that the nozzle up, because the hot fog hit the cold wall will form a water droplet, the nozzle will drop the droplets on the lamp will affect the effect of atomized cups to spray If the place has been transparent that can not be repeated many times, like fuel injection, pay attention to uniform thickness, speed and coordination. After spraying ten minutes to dry, non-stick dust, but can not scratch, let it natural curing after a few hours.

3, each time into the atomization cup of the best amount of atomizing agent between 80 to 100 ml, in order to prevent the fog cup dry, run out of available atomizer paper cups and then back up Glass bottles for the next re-use. Mist blowout time is usually heated after 5 to 6 minutes, when the mist is often not see the spray, the time one can atomize the polishing operation, to prevent waste. Two lights atomization work as much as possible to control in 2 to 3 minutes to complete, and more spray to a long time to dry and hard and prone to light wire.

4, the thickness of the headlamps generally between 4 to 5 mm, the crack layer depth is usually 0.1 to 0.4 mm or so, so fine grinding more than a few times and no defense.